ExxonMobil Exceed™ 2012RA is a metallocene linear low-density polyethylene (mLLDPE) developed for high-performance blown film applications. It is an ethylene-1-hexene copolymer that combines low density with a strong balance of toughness, impact resistance, puncture resistance, and sealing performance.

The grade offers a melt flow profile suited to blown film processing, supporting stable production across different film structures. Its combination of processing characteristics and mechanical performance gives converters greater flexibility when designing durable and lightweight packaging films.

Technical Data of mLLDPE 2012RA

Property	Typical Value	Unit	Test Method
Density	0.912	g/cm³	ASTM D792
Melt Index	2.0	g/10 min	ASTM D1238
Melt Index Condition	190°C / 2.16 kg	—	ASTM D1238
Peak Melting Temperature	114	°C	ExxonMobil Method
Vicat Softening Temperature	96	°C	ExxonMobil Method
Tensile Strength at Yield, MD	6.3	MPa	ASTM D882
Tensile Strength at Yield, TD	6.0	MPa	ASTM D882
Tensile Strength at Break, MD	70	MPa	ASTM D882
Tensile Strength at Break, TD	60	MPa	ASTM D882
Elongation at Break, MD	560	%	ASTM D882
Elongation at Break, TD	610	%	ASTM D882
Dart Drop Impact	690	g	ASTM D1709A
Elmendorf Tear Strength, MD	240	g	ASTM D1922
Elmendorf Tear Strength, TD	300	g	ASTM D1922
Puncture Force	57	N	ExxonMobil Method
Puncture Energy	5.3	J	ExxonMobil Method
45° Gloss	33	—	ASTM D2457
Haze	21	%	ASTM D1003

Why Choose Exceed 2012RA?

Low Density for Material Efficiency. The 0.912 g/cm³ density provides a lightweight material option for film converters looking to reduce film weight while retaining the mechanical properties required for packaging.
Tough and Durable Film Performance. The resin delivers a combination of impact strength, tear resistance, elongation, and puncture performance. This makes it appropriate for packaging films exposed to demanding handling conditions.
Strong Sealing Capability. Good heat-sealing and hot-tack characteristics support reliable package closure and make the grade suitable for continuous packaging processes.
Suitable for High-Performance Blown Film. Exceed 2012RA is specifically positioned for blown film applications and can support both monolayer and multilayer film designs.
Flexible Formulation Options. Because the grade does not contain slip or antiblock additives, converters can adjust film surface properties through formulation and structure design according to specific application requirements.
Broad Packaging Compatibility. Its performance profile allows the resin to serve a range of flexible packaging applications, including food packaging, heavy-duty bags, freezer films, stand-up pouches, FFS structures, and Bag-in-Box packaging.