Exceed™ 2010RA, also known as Exceed™ Flow m 1020.RA, is a metallocene linear low-density polyethylene (mLLDPE) grade designed primarily for polyethylene film production. The resin has a typical density of 0.920 g/cm³ and a melt index of 1.0 g/10 min at 190°C/2.16 kg.

Its controlled molecular structure contributes to a well-balanced profile of strength, toughness, elongation, impact resistance, and tear resistance. These properties make it well suited to flexible film applications that require dependable mechanical performance and stable extrusion processing.

Property

Typical Value

Test Method

Density

0.920 g/cm³

ASTM D792

Melt Index

1.0 g/10 min

ASTM D1238

Melt Index Condition

190°C / 2.16 kg

—

Peak Melting Temperature

Approx. 114°C

ExxonMobil Method

MD Yield Tensile Strength

1,400 psi

ASTM D882

TD Yield Tensile Strength

1,500 psi

ASTM D882

MD Tensile Strength at Break

7,900 psi

ASTM D882

TD Tensile Strength at Break

7,500 psi

ASTM D882

MD Elongation at Break

510%

ASTM D882

TD Elongation at Break

720%

ASTM D882

MD 1% Secant Modulus

29,000 psi

ASTM D882

TD 1% Secant Modulus

33,000 psi

ASTM D882

Dart Drop Impact

180 g

ASTM D1709A

MD Elmendorf Tear

130 g

ASTM D1922

TD Elmendorf Tear

550 g

ASTM D1922

45° Gloss

62

ASTM D2457

Haze

7.0%

ASTM D1003

Main Uses of Exceed™ 2010RA

  • Flexible Packaging Films. Exceed™ 2010RA works well in flexible packaging films where mechanical durability plays an important role. Its combination of tensile performance, elongation, impact resistance, and tear strength helps converters develop films for demanding packaging environments.
  • Heavy-Duty Packaging Bags. The resin can serve in heavy-duty bags and industrial packaging products that require good resistance to mechanical stress. Its toughness allows the finished film to handle demanding filling, stacking, transportation, and loading conditions.
  • Multilayer Coextruded Films. mLLDPE 2010RA can form part of multilayer coextruded film structures. Converters can combine it with other polyethylene grades or polyolefin materials to assign different functions to individual layers and achieve a more targeted balance of strength, flexibility, sealing, and processing performance.
  • Food Packaging. The grade can be used in selected food packaging structures, including flexible and multilayer films. Its mechanical properties contribute to packaging durability during production, filling, distribution, and consumer handling. Food-contact suitability should always be evaluated according to the applicable regulations, market requirements, final formulation, and intended end use.
  • Agricultural Films. Exceed™ 2010RA is also suitable for selected agricultural film applications. Its combination of toughness and elongation can help films withstand mechanical stress during installation and service.
  • Stretch and Shrink Films. This material can also support stretch film and shrink film formulations where film strength and resistance to mechanical damage are important. Processors can adjust the formulation and processing conditions according to the required thickness, film structure, and end-use performance.

Product Characteristics

  • Balanced Mechanical Performance
  • High Impact Resistance
  • Good Tear Resistance
  • Controlled Stiffness and Flexibility
  • Film Processing Compatibility