Borouge BJ368MO is a heterophasic polypropylene copolymer characterized by very high flow, and optimum combination of high stiffness and impact strength. The material is nucleated with Borstar Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. PP BJ368MO has both good antistatic performance and mould release properties.
Special Features of Borouge PP BJ368MO
- Very good stiffness and impact balance
- Good flow behaviour
- Reduced cycle time and increased output
Main Applications of BJ368MO
- Thin wall containers
- Food packaging
- Small size ice cream containers
| Property |
Typical Value |
Test Method |
| Density |
900-910kg/m³ |
ISO 1183 |
| Melt Flow Rate (230°C/2.16kg) |
70g/10min |
ISO 1133 |
| Tensile Modulus (1mm/min) |
1500MPa |
ISO 527-2 |
| Tensile Strain at Yield (50mm/min) |
4% |
ISO 527-2 |
| Tensile Stress at Yield (50mm/min) |
25MPa |
ISO 527-2 |
| Flexural Modulus |
1500MPa |
ISO 178 |
| Tensile Strain at Yield |
4% |
ASTM D638 |
| Tensile Stress at Yield |
25MPa |
ASTM D638 |
| Flexural Modulus(by 1% secant) |
1450MPa |
ASTM D790A |
| Charpy Impact Strength, notched (23°C) |
5,5kJ/m² |
ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) |
3,5kJ/m² |
ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) |
55J/m |
ASTM D256 |
| IZOD Impact Strength, notched (-20°C) |
40J/m |
ASTM D256 |
| Heat Deflection Temperature(0,45MPa)** |
102°C |
ISO 75-2 |
| Vicat Softening Temperature(Method A)*** |
150°C |
ISO 306 |
| Hardness, Rockwell(R-scale) |
92 |
ISO 2039-2 |